| Typical Characteristics | |||
| Name | Method | Units | Braycote 803 |
| Unworked Penetration | ASTM D217/IP50 | 0.1mm | 286 |
| Worked Penetration (60 Strokes @ 25ºC) |
ISO 2137 / ASTM D217 | 0.1mm |
283 |
| Evaporation Loss (22 hrs @ 204ºC) |
ASTM D2595 |
%wt |
0.33 |
| Oil Separation (30hrs @ 204ºC) |
FTM 321.2/ASTM D6184 | %wt |
8.93 |
| Copper Corrosion (22hrs, 100ºC) |
ASTM D4048 |
Rating |
1b |
| Four Ball Wear Test - Wear Scar Diameter (40kgf/75ºC/1200rpm/1hr) |
ISO 51350 / ASTM D2266 |
mm |
0.70 |
| Four Ball Weld Load Test - Weld Point | ISO 11008 / ASTM D2596 | kgf | 500 |
| Dropping point | ASTM D2265 | ºC | 216 |
| Low Temperature Torque - starting torque | ASTM D1478 | N/m | 0.22 |
| Low temperature Torque - torque after 60 mins | ASTM D1478 | N/m | 0.13 |
| Density of finished grease @ 15ºC | In-house test | lb/gal | 15.71 |
| Base Oil Viscosity @ 20ºC | ISO 3104 / ASTM D445 | mm²/s | 440 |
| Base Oil Viscosity @ 40ºC | ISO 3104 / ASTM D445 | mm²/s | 187 |
| Base Oil Viscosity @ 100ºC | ISO 3104 / ASTM D445 | mm²/s | 23 |
| Viscosity Index | ISO 2909 / ASTM D2270 | - | 225 |
| Knudsen Vapor Pressure @ 20ºC | - | Pa | <0.0000000133 |
| Knudsen Vapor Pressure @ 100ºC | - | Pa | 0.0000133 |
| Pour Point | ISO 3016 / ASTM D97 | ºC | <-60 |
Braycote 803 was developed for use in applications where long term exposure to high temperature or high vacuum is expected. This product is fully compatible for use in both direct and indirect contact with liquid and gaseous oxygen (LOX/ GOX). Braycote 803 is stable with exposure to strong acids and oxidizers. Perfluorinated greases, in general, exhibit excellent shelf lives due to their intrinsic inertness. Below -62ºC to above 260ºC (below -80ºF to above 499ºF). Lower temperature operation below -62ºC (-80ºF) is possible where adequate torque is available.
Braycote 803 is compatible with most commonly used construction materials including metals, plastics and elastomers. This product may be adversely affected by Lewis Acids such as aluminum chloride, at elevated temperatures. Newly exposed rubbing surfaces of aluminum, magnesium or titanium alloys at elevated temperatures may react with Braycote 803 under certain conditions. Such systems should be thoroughly evaluated. Surfaces must be well cleaned of organic rust inhibitors prior to grease application to ensure proper lubrication.